Novel catalyst system and the use thereof

ABSTRACT

The invention relates to a catalyst system, containing at least one metallocene, at least one co-catalyst, at least one supporting material and optionally additional organometallic compounds. The catalyst system can be used advantageously for polymerising olefins, as it obviates the use of aluminoxanes, such as methylaluminoxane (MAO), which is conventionally used in excess quantities as a co-catalyst, whilst at the same time producing strong catalyst activity and excellent polymer morphology.

[0001] The present invention relates to a catalyst system comprising at least one metallocene, at least one cocatalyst, at least one support material and, if desired, further organometallic compounds.

[0002] The catalyst system can advantageously be used for the polymerization of olefins and displays a high catalyst activity and gives a good polymer morphology without it being necessary to use aluminoxanes such as methylaluminoxane (MAO), which usually has to be used in high excess, as cocatalyst. Furthermore, the use of starting materials which could potentially be toxic is avoided.

[0003] For industrial utilization of metallocene catalysts, the catalyst system has to be made heterogeneous in order to ensure an appropriate morphology of the resulting polymers. Here, it is found to be advantageous to bind the components of the catalyst system covalently to the support so as to avoid “bleeding” of the active component from the support and thus an adverse effect on the polymer morphology.

[0004] A series of patents (see, for example, WO-96/23005, DE-A 19804970, DE-A 19823172, DE-A 19744102, DE-A 19757540) describe catalyst systems in which the cocatalyst, namely an organoelement compound, is bound covalently to the support material with formation of an ammonium salt. A disadvantage of these systems is that they preferably employ tertiary anilines as organic bases and these are compounds which require particular protective measures in catalyst production because of their possible toxic or gene-toxic potential.

[0005] It is an object of the present invention to provide a catalyst system based on the covalent fixing of a cocatalyst to a support, which system avoids the disadvantages of the prior art. We have found that this object is achieved by a catalyst system based on a specific class of toxicologically acceptable Lewis bases, which unexpectedly displays high polymerization activities and gives a good polymer morphology.

[0006] The catalyst system of the present invention comprises

[0007] a) at least one organometallic compound,

[0008] b) at least one Lewis base,

[0009] c) at least one support and

[0010] d) at least one organoelement compound which is the reaction product of at least one compound of the formula (VI) with at least one compound of the formula (IX),

[0011]  where

[0012] R⁷ can be a hydrogen atom or a boron-free C₁-C₄₀ group such as C₁-C₂₀-alkyl, C₆-C₂₀-aryl, C₇-C₄₀-arylalkyl, C₇-C₄₀-alkylaryl,

[0013] R⁴ and R⁵ are identical or different and are each a hydrogen atom, a halogen atom or a C₁-C₄₀ group or R⁴ is an —OSiR₃ group, where R are identical or different and are as defined for R⁵,

[0014] X is an element of main group VI of the Periodic Table of the Elements or an NR group, where R is a hydrogen atom or a C₁-C₂₀-hydrocarbon radical such as C₁-C₂₀-alkyl or C₁-C₂₀-aryl,

[0015] f is an integer from 0 to 3

[0016] g is an integer from 0 to 3, where f+g is not equal to 0,

[0017] h is an integer from 1 to 10,

[0018] where the organoelement compound is covalently bound to the support,

[0019] wherein the Lewis base has the formula I,

M¹R¹R²R³  (I)

[0020]  where

[0021] M¹ is an element of main group V of the Periodic Table of the Elements,

[0022] R¹, R² and R³ are identical or different and are each a hydrogen atom, a C₁-C₂₀-alkyl group, a C₁-C₂₀-haloalkyl group or a C₇-C₄₀-arylalkyl group, where two radicals or all three radicals R¹, R² and R³ may be joined to one another via C₂-C₂₀ units, where at least one radical R¹, R² or R³ is a C₇-C₄₀-arylalkyl group,

[0023] and, if desired,

[0024] e) at least one organometallic compound of the formula III

[M³R⁶ _(d)]_(e)  (III)

[0025]  where

[0026] M³ is an element of main group I, II or III of the Periodic Table of the Elements,

[0027] R⁶ are identical or different and are each a hydrogen atom, a halogen atom or a C₁-C₄₀ group, in particular C₁-C₂₀-alkyl, C₆-C₄₀-aryl, C₇-C₄₀-arylalkyl or C₇-C₄₀-alkylaryl,

[0028] d is an integer from 1 to 3 and

[0029] e is an integer from 1 to 4.

[0030] Preference is given to Lewis bases of the formula (I) in which R¹, R² and R³ are identical or different and are each a benzylic group.

[0031] Examples of Lewis bases of the formula (I) are

[0032] N,N-diethylbenzylamine, N,N-dimethylbenzylamine,

[0033] N-benzyldimethylamine, N-benzyldiethylamine, N-benzylbutylamine,

[0034] N-benzyl tertbutylamine, N-benzylisopropylamine,

[0035] N-benzylmethylamine, N-benzylethylamine,

[0036] N-benzyl-1-phenylethylamine, N-benzyl-2-phenylethylamine,

[0037] N,N-dimethylbenzylamine, N,N-diethylbenzylamine,

[0038] N-methyl-N-ethylbenzylamine, N-methyldibenzylamine,

[0039] N-ethyldi(benzyl)amine.

[0040] Examples of particularly preferred bases are benzylamine, N-benzyldimethylamine, N-benzyldiethylamine, N-benzylbutylamine, N-benzyl tert-butylamine, N-benzylisopropylamine, N-benzylmethylamine, N-benzylethylamine, N-benzyl-1-phenylethylamine or N-benzyl-2-phenylethylamine.

[0041] The support is a porous inorganic or organic solid. The support preferably comprises at least one inorganic oxide such as silicon oxide, aluminum oxide, aluminosilicates, zeolites, MgO, ZrO₂, TiO₂, B₂O₃, CaO, ZnO, ThO₂, Na₂CO₃, K₂CO₃, CaCO₃, MgCl₂, Na₂SO₄, Al₂(SO₄)₃, BaSO₄, KNO₃, Mg(NO₃)₂, Al(NO₃)₃, Na₂O, K₂O, Li₂O, or mixed oxides, in particular silicon oxide and/or aluminum oxide and/or Mg-Al mixed oxide. The support may also comprise at least one polymer, e.g. a homopolymer or copolymer, crosslinked polymer or a polymer blend. Examples of polymers are polyethylene, polypropylene, polybutene, polystyrene, divinylbenzene-crosslinked polystyrene, polyvinyl chloride, acrylonitrile-butadiene-styrene copolymer, polyamide, polymethacrylate, polycarbonate, polyester, polyacetal or polyvinyl alcohol.

[0042] The support has a specific surface area in the range from 10 to 1000 m²/g, preferably from 150 to 500 m²/g. The mean particle size of the support is from 1 to 500 μm, preferably from 5 to 350 μm, particularly preferably from 10 to 200 μm.

[0043] The support is preferably porous with a pore volume of from 0.5 to 4.0 ml/g, preferably from 1.0 to 3.5 ml/g. A porous support has a certain proportion of voids (pore volume). The shape of the pores is usually irregular, frequently spherical. The pores can be connected to one another by small pore openings. The pore diameter is preferably from about 2 to 50 nm. The particle shape of the porous support depends on the after-treatment and can be irregular or spherical. The particle size of the support can be set to any desired value, for example, by cryogenic milling and/or sieving.

[0044] The organometallic compounds of the formula (III) are preferably uncharged Lewis acids in which M⁴ is lithium, magnesium and/or aluminum, in particular aluminum. Examples of preferred organometallic compounds of the formula (III) are trimethylaluminum, triethylaluminum, triisopropylaluminum, trihexylaluminum, trioctylaluminum, tri-n-butylaluminum, triisobutylaluminum,tri-n-propylaluminum, triisoprenylaluminum, dimethylaluminum monochloride, diethylaluminum monochloride, diisobutylaluminum monochloride, methylaluminum sesquichloride, ethylaluminum sesquichloride, dimethylaluminum hydride, diethylaluminum hydride, diisopropylaluminum hydride, dimethylaluminum trimethylsiloxide, dimethylaluminum triethylsiloxide, phenylalane, pentafluorophenylalane and o-tolylalane.

[0045] The metallocene compounds present in the catalyst system of the present invention can be, for example, bridged or unbridged biscyclopentadienyl complexes as are described, for example, in EP-A-0,129,368, EP-A-0,561,479, EP-A-0,545,304 and EP-A-0,576,970, monocyclopentadienyl complexes such as bridged amidocyclopentadienyl complexes as are described, for example, in EP-A-0,416,815, polycyclic cyclopentadienyl complexes as are described, for example, in EP-A-0,632,063, p-ligand-substituted tetrahydropentalenes as are described, for example, in EP-A-0,659,758 or π-ligand-substituted tetrahydroindenes as are described, for example, in EP-A-0,661,300.

[0046] It is also possible to use organometallic compounds in which the complexing ligand does not contain a cyclopentadienyl ligand. Examples of such compounds are diamine complexes of metals of transition groups III and IV of the Periodic Table of the Elements, as are described, for example, by D. H. McConville et al, Macromolecules, 1996, 29, 5241 and D. H. McConville et al, J. Am. Chem. Soc., 1996, 118, 10008. Diimine complexes of metals of transition group VIII of the Periodic Table of the Elements (e.g. Ni²⁺ or Pd²⁺ complexes) as are described by Brookhart et al, J. Am. Chem. Soc. 1995, 117, 6414 and Brookhart et al, J. Am. Chem. Soc., 1996, 118, 267, can also be used. Furthermore, it is possible to use 2,6-bis(imino)pyridyl complexes of metals of transition group VIII of the Periodic Table of the Elements (e.g. Co²⁺ or Fe²⁺ complexes), as are described by Brookhart et al, J. Am. Chem. Soc. 1998, 120, 4049 and Gibson et al, Chem. Commun. 1998, 849. It is also possible to use metallocene compounds whose complexing ligand contains heterocycles. Examples are described in WO 98/22486.

[0047] Preferred metallocene compounds are unbridged or bridged compounds of the formula (X),

[0048] where

[0049] M⁴ is a metal of transition group III, IV, V or VI of the Periodic Table of the Elements, in particular Ti, Zr or Hf.

[0050] R⁸ are identical or different and are each a hydrogen atom or SiR₃, where R are identical or different and are each a hydrogen atom or a C₁-C₄₀ group such as C₁-C₂₀-alkyl, C₁-C₁₀-fluoroalkyl, C₁-C₁₀-alkoxy, C₆-C₂₀-aryl, C₆-C₁₀-fluoroaryl, C₆-C₁₀-aryloxy, C₂-C₁₀-alkenyl, C₇-C₄₀-arylalkyl, C₇-C₄₀-alkylaryl or C₈-C₄₀-arylalkenyl, or R⁸ are a C₁-C₃₀ group such as C₁-C₂₅-alkyl, e.g. methyl, ethyl, tert-butyl, cyclohexyl or octyl, C₂-C₂₅-alkenyl, C₃-C₁₅-alkylalkenyl, C₆-C₂₄-aryl, C₄-C₂₄-heteroaryl such as pyridyl, furyl or quinolyl, C₇-C₃₀-arylalkyl, C₅-C₃₀-heteroarylalkyl, C₇-C₃₀-alkylaryl, C₅-C₃₀-alkylheteroaryl, fluorinated C₁-C₂₅-alkyl, fluorinated C₆-C₂₄-aryl, fluorinated C₇-C₃₀-arylalkyl, fluorinated C₇-C₃₀-alkylaryl or C₁-C₁₂-alkoxy, or two or more radicals R⁸ may be joined to one another in such a way that the radicals R⁸ and the atoms of the cyclopentadienyl ring which connect them form a carbocyclic or heterocyclic C₄-C₂₄ ring system which may in turn be substituted,

[0051] R⁹ are identical or different and are each a hydrogen atom or SiR₃, where R are identical or different and are each a hydrogen atom or a C₁-C₄₀ group such as C₁-C₂₀-alkyl, C₁-C₁₀-fluoroalkyl, C₁-C₁₀-alkoxy, C₆-C₁₄-aryl, C₆-C₁₀-fluoroaryl, C₆-C₁₀-aryloxy, C₂-C₁₀-alkenyl, C₇-C₄₀-arylalkyl, C₇-C₄₀-alkylaryl or C₈-C₄₀-arylalkenyl, or R⁹ are a C₁-C₃₀ group such as C₁-C₂₅-alkyl, e.g. methyl, ethyl, tert-butyl, cyclohexyl or octyl, C₂-C₂₅-alkenyl, C₃-C₁₅-alkylalkenyl, C₆-C₂₄-aryl, C₅-C₂₄-heteroaryl, e.g. pyridyl, furyl or quinolyl, C₇-C₃₀-arylalkyl, C₇-C₃₀-alkylaryl, fluorinated C₁-C₂₅-alkyl, fluorinated C₆-C₂₄-aryl, fluorinated C₇-C₃₀-arylalkyl, fluorinated C₇-C₃₀-alkylaryl or C₁-C₁₂-alkoxy, or two or more radicals R⁹ may be joined to one another in such a way that the radicals R⁹ and the atoms of the cyclopentadienyl ring which connect them form a carbocyclic or heterocyclic C₄-C₂₄ ring system which may in turn be substituted,

[0052] l is 5 when v=0 and l is 4 when v=1,

[0053] m is 5 when v=0 and m is 4 when v=1,

[0054] L¹ may be identical or different and are each a hydrogen atom, a C₁-C₁₀-hydrocarbon group such as C₁-C₁₀-alkyl or C₆-C₁₀-aryl, a halogen atom or OR¹², SR¹², OSiR¹² ₃, SiR¹¹ ₃, PR¹¹ ₂ or NR¹¹ ₂, where, R¹¹ is a halogen atom, a C₁-C₁₀-alkyl group, a C₁-C₁₀-alkoxy group, a halogenated C₁-C₁₀-alkyl group, a C₆-C₂₀-aryl group, a C₇-C₂₀-alkylaryl group, a C₇-C₂₀-arylalkyl group or a halogenated C₆-C₂₀-aryl group, or L¹ are a toluenesulfonyl, trifluoroacetyl, trifluoroacetoxyl, trifluoromethanesulfonyl, nonafluorobutanesulfonyl or 2,2,2-trifluoroethanesulfonyl group,

[0055] o is an integer from 1 to 4, preferably 2,

[0056] Z is a bridging structural element between the two cyclopentadienyl rings and v is 0 or 1.

[0057] Examples of Z are MR¹⁰R¹¹ groups, where M is carbon, silicon, germanium or tin and R¹⁰ and R¹¹ are identical or different and are each a C₁-C₂₀-hydrocarbon-containing group such as C₁-C₁₀-alkyl, C₆-C₁₄-aryl or trimethylsilyl. Z is preferably CH₂, CH₂CH₂, CH(CH₃)CH₂, CH(C₄H₉)C(CH₃)₂, C(CH₃)₂, (CH₃)₂Si, (CH₃)₂Ge, (CH₃)₂Sn, (C₆H₅)₂Si, (C₆H₅)(CH₃)Si, (C₆H₅)₂Ge, (C₆H₅)₂Sn, (CH₂)₄Si, CH₂Si(CH₃)₂, o-C₆H₄ or 2,2′-(C₆H₄)₂. Z together with one or more radicals R⁸ and/or R⁹ may also form a monocyclic or polycyclic ring system.

[0058] Preference is given to chiral bridged metallocene compounds of the formula (X), in particular those in which v is 1 and one or both cyclopentadienyl rings are substituted so that they form an indenyl ring, a sulfur-, nitrogen- or oxygen-containing heterocycle analogous to indenyl or a sulfur-, nitrogen- or oxygen-containing heterocycle analogous to pentalene.

[0059] These rings are preferably substituted, in particular [in accordance with the nomenclature in the formulae (XIa) and (XIb)] in the 2 position, 4 position, 2,4 positions, 2,4,5 positions, 2,4,6 positions, 2,4,7 positions or 2,4,5,6 positions, by C₁-C₂₀ groups such as C₁-C₁₀-alkyl or C₆-C₂₀-aryl, where two or more substituents of the rings mentioned may together form a ring system.

[0060] Chiral bridged metallocene compounds of the formula (X) can be used as pure racemic or pseudo-racemic or pure meso or pseudo-meso compounds. However, it is also possible to use mixtures of a racemic or pseudo-racemic compound and a meso or pseudo-meso compound.

[0061] Examples of metallocene compounds are:

[0062] dimethylsilanediylbis(indenyl)zirconium dichloride

[0063] dimethylsilanediylbis(4-naphthylindenyl)zirconium dichloride

[0064] dimethylsilanediylbis(2-methylbenzoindenyl)zirconium dichloride

[0065] dimethylsilanediylbis(2-methylindenyl)zirconium dichloride

[0066] dimethylsilanediylbis(2-methyl-4-(1-naphthyl)indenyl)zirconium dichloride

[0067] dimethylsilanediylbis(2-methyl-4-(2-naphthyl)indenyl)zirconium dichloride

[0068] dimethylsilanediylbis(2-methyl-4-phenylindenyl)zirconium dichloride

[0069] dimethylsilanediylbis(2-methyl-4-t-butylindenyl)zirconium dichloride

[0070] dimethylsilanediylbis(2-methyl-4-isopropylindenyl)zirconium dichloride

[0071] dimethylsilanediylbis(2-methyl-4-ethylindenyl)zirconium dichloride

[0072] dimethylsilanediylbis(2-methyl-4-a-acenaphthindenyl)zirconium dichloride

[0073] dimethylsilanediylbis(2,4-dimethylindenyl)zirconium dichloride

[0074] dimethylsilanediylbis(2-ethylindenyl)zirconium dichloride

[0075] dimethylsilanediylbis(2-ethyl-4-ethylindenyl)zirconium dichloride

[0076] dimethylsilanediylbis(2-ethyl-4-phenylindenyl)zirconium dichloride

[0077] dimethylsilanediylbis(2-methyl-4,5-benzoindenyl)zirconium dichloride

[0078] dimethylsilanediylbis(2-methyl-4,6-diisopropylindenyl)zirconium dichloride

[0079] dimethylsilanediylbis (2-methyl-4,5-diisopropylindenyl)zirconium dichloride

[0080] dimethylsilanediylbis(2,4,6-trimethylindenyl)zirconium dichloride

[0081] dimethylsilanediylbis(2,5,6-trimethylindenyl)zirconium dichloride

[0082] dimethylsilanediylbis(2,4,7-trimethylindenyl)zirconium dichloride

[0083] dimethylsilanediylbis(2-methyl-5-isobutylindenyl)zirconium dichloride

[0084] dimethylsilanediylbis(2-methyl-5-t-butylindenyl)zirconium dichloride

[0085] methyl(phenyl)silanediylbis(2-methyl-4-phenylindenyl)zirconium dichloride

[0086] methyl(phenyl)silanediylbis(2-methyl-4,6-diisopropylindenyl)zirconium dichloride

[0087] methyl(phenyl)silanediylbis(2-methyl-4-isopropylindenyl)zirconium dichloride

[0088] methyl(phenyl)silanediylbis(2-methyl-4,5-benzoindenyl)zirconium dichloride

[0089] methyl(phenyl)silanediylbis(2-methyl-4,5-(methylbenzo)indenyl)zirconium dichloride

[0090] methyl(phenyl)silanediylbis(2-methyl-4,5-(tetramethylbenzo)indenyl)zirconium dichloride

[0091] methyl(phenyl)silanediylbis(2-methyl-4-α-acenaphthindenyl)zirconium dichloride

[0092] methyl(phenyl)silanediylbis(2-methylindenyl)zirconium dichloride

[0093] methyl(phenyl)silanediylbis(2-methyl-5-isobutylindenyl)zirconium dichloride

[0094] 1,2-ethanediylbis(2-methyl-4-phenylindenyl)zirconium dichloride

[0095] 1,4-butanediylbis(2-methyl-4-phenylindenyl)zirconium dichloride

[0096] 1,2-ethanediylbis (2-methyl-4,6 diisopropylindenyl) zirconium dichloride

[0097] 1,4-butanediylbis(2-methyl-4-isopropylindenyl)zirconium dichloride

[0098] 1,4-butanediylbis(2-methyl-4,5-benzoindenyl)zirconium dichloride

[0099] 1,2-ethanediylbis(2-methyl-4,5-benzoindenyl)zirconium dichloride

[0100] 1,2-ethanediylbis(2,4,7-trimethylindenyl)zirconium dichloride

[0101] 1,2-ethanediylbis(2-methylindenyl)zirconium dichloride

[0102] 1,4-butanediylbis(2-methylindenyl)zirconium dichloride

[0103] [4-(η⁵-cyclopentadienyl)-4,6,6-trimethyl-(η⁵-4,5-tetrahydropentalene)]dichlorozirconium

[0104] [4-(η⁵-3′-trimethylsilylcyclopentadienyl)-4,6,6-trimethyl(η⁵-4,5-tetrahydropentalene)]dichlorozirconium

[0105] [4-(η⁵-3′-isopropylcyclopentadienyl)-4,6,6-trimethyl(η⁵-4,5-tetrahydropentalene)]dichlorozirconium

[0106] [4-(η⁵-cyclopentadienyl)-4,7,7-trimethyl(η⁵-4,5,6,7-tetrahydroindenyl)]dichlorotitanium

[0107] [4-(η⁵-cyclopentadienyl)-4,7,7-trimethyl(η⁵-4,5,6,7-tetrahydroindenyl)]dichlorozirconium

[0108] [4-(η⁵-cyclopentadienyl)-4,7,7-trimethyl(η⁵-4,5,6,7-tetrahydroindenyl)]dichlorohafnium

[0109] [4-(η⁵-3=-tert-butylcyclopentadienyl)-4,7,7-trimethyl(η⁵-4,5,6,7-tetrahydroindenyl)]dichlorotitanium

[0110] 4-(η⁵-3=-isopropylcyclopentadienyl)-4,7,7-trimethyl(η⁵-4,5,6,7-tetrahydroindenyl)]dichlorotitanium

[0111] 4-(η⁵-3=-methylcyclopentadienyl)-4,7,7-trimethyl(η⁵-4,5,6,7-tetrahydroindenyl)]dichlorotitanium

[0112] 4-(η⁵-3=-trimethylsilylcyclopentadienyl)-2-trimethylsilyl-4,7,7-trimethyl(η⁵-4,5,6,7-tetrahydroindenyl)]dichlorotitanium

[0113] 4-(η⁵-3=-tert-butylcyclopentadienyl)-4,7,7-trimethyl(η⁵-4,5,6,7-tetrahydroindenyl)]dichlorozirconium

[0114] (tert-butylamido)(tetramethyl-η⁵-cyclopentadienyl)dimethyl-silyldichlorotitanium

[0115] (tert-butylamido)(tetramethyl-η⁵-cyclopentadienyl)-1,2-ethane-diyldichlorotitanium

[0116] (methylamido)(tetramethyl-η⁵-cyclopentadienyl)dimethylsilyl-dichlorotitanium

[0117] (methylamido)(tetramethyl-η⁵-cyclopentadienyl)-1,2-ethanediyl-dichlorotitanium

[0118] (tert-butylamido)(2,4-dimethyl-2,4-pentadien-1-yl)dimethyl-silyldichlorotitanium

[0119] bis(cyclopentadienyl)zirconium dichloride

[0120] bis(n-butylcyclopentadienyl)zirconium dichloride

[0121] bis(1,3-dimethylcyclopentadienyl)zirconium dichloride

[0122] tetrachloro-[1-[bis(η⁵-1H-inden-1-ylidene)methylsilyl]-3-(η⁵-cyclopenta-2,4-dien-1-ylidene)-3-(η⁵-9H-fluoren-9-yliden)butane]-dizirconium

[0123] tetrachloro-[2-[bis(η⁵-2-methyl-1H-inden-1-ylidene)methoxysilyl]-5-(η⁵-2,3,4,5-tetramethylcyclopenta-2,4-dien-1-ylidene)-5-(η⁵-9H-fluoren-9-ylidene)hexane]dizirconium

[0124] tetrachloro-[1-[bis(η⁵-1H-inden-1-ylidene)methylsilyl]-6-(η⁵-cyclopenta-2,4-dien-1-ylidene)-6-(η⁵-9H-fluoren-9-ylidene)-3-oxa-heptane]dizirconium

[0125] dimethylsilanediylbis(2-methyl-4-(4′-tert-butylphenylindenyl)zirconium dichloride

[0126] dimethylsilanediylbis(2-methyl-4-(4′-methylphenylindenyl)zirconium dichloride

[0127] dimethylsilanediylbis(2-methyl-4-(4′-ethylphenylindenyl)zirconium dichloride

[0128] dimethylsilanediylbis(2-methyl-4-(4′-trifluoromethylphenylindenyl)zirconium dichloride

[0129] dimethylsilanediylbis(2-methyl-4-(4′-methoxyphenylindenyl)zirconium dichloride

[0130] dimethylsilanediylbis(2-ethyl-4-(4′-tert-butylphenylindenyl)zirconium dichloride

[0131] dimethylsilanediylbis(2-ethyl-4-(4′-methylphenylindenyl)zirconium dichloride

[0132] dimethylsilanediylbis(2-ethyl-4-(4′-ethylphenylindenyl)zirconium dichloride

[0133] dimethylsilanediylbis(2-ethyl-4-(4′-trifluoromethylphenylindenyl)zirconium dichloride

[0134] dimethylsilanediylbis(2-ethyl-4-(4′-methoxyphenylindenyl)zirconium dichloride

[0135] dimethylsilanediylbis(2-methyl-4-(4′-tert-butylphenylindenyl)dimethyl zirconium

[0136] dimethylsilanediylbis(2-methyl-4-(4′-methylphenylindenyl)dimethylzirconium

[0137] dimethylsilanediylbis(2-methyl-4-(4′-ethylphenylindenyl)dimethylzirconium

[0138] dimethylsilanediylbis(2-methyl-4-(4′-trifluoromethylphenylindenyl)dimethylzirconium

[0139] dimethylsilanediylbis(2-methyl-4-(4′-methoxyphenylindenyl)dimethylzirconium

[0140] dimethylsilanediylbis(2-ethyl-4-(4′-tert-butylphenylindenyl)dimethylzirconium

[0141] dimethylsilanediylbis(2-ethyl-4-(4′-methylphenylindenyl)dimethylzirconium

[0142] dimethylsilanediylbis(2-ethyl-4-(4′-ethylphenylindenyl)dimethylzirconium

[0143] dimethylsilanediylbis(2-ethyl-4-(4′-trifluoromethylphenylindenyl)dimethylzirconium

[0144] dimethylsilanediylbis(2-ethyl-4-(4′-methoxyphenylindenyl)dimethylzirconium

[0145] dimethylsilanediylbis(2-methyl-4-(4′-trimethylsilylphenylindenyl) zirconium dichloride

[0146] dimethylsilanediylbis(2-methyl-4-(4′-trimethylsilylphenylindenyl) dimethylzirconium

[0147] dimethylsilanediylbis(2-ethyl-4-(4′-trimethylsilylphenylindenyl)zirconium dichloride

[0148] dimethylsilanediylbis(2-ethyl-4-(4′-trimethylsilylphenylindenyl)dimethylzirconium

[0149] dimethylsilanediylbis(2-methyl-4-(4′-tert-butylphenyl)indenyl)hafnium dichloride

[0150] dimethylsilanediylbis(2-methyl-4-(4′-tert-butylphenyl)indenyl)titanium dichloride

[0151] dimethylsilanediylbis(2-methyl-4-(4′-methylphenyl)indenyl)zirconium dichloride

[0152] dimethylsilanediylbis(2-methyl-4-(4′-n-propylphenyl)indenyl)zirconium dichloride

[0153] dimethylsilanediylbis(2-methyl-4-(4′-n-butylphenyl)indenyl)zirconium dichloride

[0154] dimethylsilanediylbis(2-methyl-4-(4′-hexylphenyl)indenyl)zirconium dichloride

[0155] dimethylsilanediylbis(2-methyl-4-(4′-sec-butylphenyl)indenyl)zirconium dichloride

[0156] dimethylsilanediylbis(2-ethyl-4-phenyl)indenyl)zirconium dichloride

[0157] dimethylsilanediylbis(2-ethyl-4-(4′-methylphenyl)indenyl)zirconium dichloride

[0158] dimethylsilanediylbis(2-ethyl-4-(4′-ethylphenyl)indenyl)zirconium dichloride

[0159] dimethylsilanediylbis(2-ethyl-4-(4′-n-propylphenyl)indenyl)zirconium dichloride

[0160] dimethylsilanediylbis(2-ethyl-4-(4′-n-butylphenyl)indenyl)zirconium dichloride

[0161] dimethylsilanediylbis(2-ethyl-4-(4′-hexylphenyl)indenyl)zirconium dichloride

[0162] dimethylsilanediylbis(2-ethyl-4-(4′-pentylphenyl)indenyl)zirconium dichloride

[0163] dimethylsilanediylbis(2-ethyl-4-(4′-cyclohexylphenyl)indenyl)zirconium dichloride

[0164] dimethylsilanediylbis(2-ethyl-4-(4′-sec-butylphenyl)indenyl)zirconium dichloride

[0165] dimethylsilanediylbis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)zirconium dichloride

[0166] dimethylsilanediylbis(2-n-propyl-4-phenyl)indenyl)zirconium dichloride

[0167] dimethylsilanediylbis(2-n-propyl-4-(4′-methylphenyl)indenyl)zirconium dichloride

[0168] dimethylsilanediylbis(2-n-propyl-4-(4′-ethylphenyl)indenyl)zirconium dichloride

[0169] dimethylsilanediylbis(2-n-propyl-4-(4′-iso-propylphenyl)indenyl)zirconium dichloride

[0170] dimethylsilanediylbis(2-n-propyl-4-(4′-n-butylphenyl)indenyl)zirconium dichloride

[0171] dimethylsilanediylbis(2-n-propyl-4-(4′-hexylphenyl)indenyl)zirconium dichloride

[0172] dimethylsilanediylbis(2-n-propyl-4-(4′-cyclohexylphenyl)indenyl)zirconium dichloride

[0173] dimethylsilanediylbis(2-n-propyl-4-(4′-sec-butylphenyl)indenyl)zirconium dichloride

[0174] dimethylsilanediylbis(2-n-propyl-4-(4′-tert-butylphenyl)indenyl)zirconium dichloride

[0175] dimethylsilanediylbis(2-n-butyl-4-phenyl)indenyl)zirconium dichloride

[0176] dimethylsilanediylbis(2-n-butyl-4-(4′-methylphenyl)indenyl)zirconium dichloride

[0177] dimethylsilanediylbis(2-n-butyl-4-(4′-ethylphenyl)indenyl)zirconium dichloride

[0178] dimethylsilanediylbis(2-n-butyl-4-(4′-n-propylphenyl)indenyl)zirconium dichloride

[0179] dimethylsilanediylbis(2-n-butyl-4-(4′-iso-propylphenyl)indenyl)zirconium dichloride

[0180] dimethylsilanediylbis(2-n-butyl-4-(4′-n-butylphenyl)indenyl)zirconium dichloride

[0181] dimethylsilanediylbis(2-n-butyl-4-(4′-hexylphenyl)indenyl)zirconium dichloride

[0182] dimethylsilanediylbis(2-n-butyl-4-(4′-cyclohexylphenyl)indenyl)zirconium dichloride

[0183] dimethylsilanediylbis(2-n-butyl-4-(4′-sec-butylphenyl)indenyl)zirconium dichloride

[0184] dimethylsilanediylbis(2-n-butyl-4-(4′-tert-butylphenyl)indenyl)zirconium dichloride

[0185] dimethylsilanediylbis(2-hexyl-4-phenyl)indenyl)zirconium dichloride

[0186] dimethylsilanediylbis(2-hexyl-4-(4′-methylphenyl)indenyl)zirconium dichloride

[0187] dimethylsilanediylbis(2-hexyl-4-(4′-ethylphenyl)indenyl)zirconium dichloride

[0188] dimethylsilanediylbis(2-hexyl-4-(4′-n-propylphenyl)indenyl)zirconium dichloride

[0189] dimethylsilanediylbis(2-hexyl-4-(4′-iso-propylphenyl)indenyl)zirconium dichloride

[0190] dimethylsilanediylbis(2-hexyl-4-(4′-n-butylphenyl)indenyl)zirconium dichloride

[0191] dimethylsilanediylbis(2-hexyl-4-(4′-hexylphenyl)indenyl)zirconium dichloride

[0192] dimethylsilanediylbis(2-hexyl-4-(4′-cyclohexylphenyl)indenyl)zirconium dichloride

[0193] dimethylsilanediylbis(2-hexyl-4-(4′-sec-butylphenyl)indenyl)zirconium dichloride

[0194] dimethylsilanediylbis(2-hexyl-4-(4′-tert-butylphenyl)indenyl)zirconium dichloride

[0195] dimethylsilanediylbis(2-methyl-4-(4′-tert-butylphenyl)indenyl)zirconium bis(dimethylamide)

[0196] dimethylsilanediylbis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)dibenzylzirconium

[0197] dimethylsilanediylbis(2-methyl-4-(4′-tert-butylphenyl)indenyl)dimethylzirconium

[0198] dimethylgermanediylbis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)zirconium dichloride

[0199] dimethylgermanediylbis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)hafnium dichloride

[0200] dimethylgermanediylbis(2-propyl-4-(4′-tert-butylphenyl)indenyl)titanium dichloride

[0201] dimethylgermanediylbis(2-methyl-4-(4′-tert-butylphenyl)indenyl)zirconium dichloride

[0202] ethylidenebis(2-ethyl-4-phenyl)indenyl)zirconium dichloride

[0203] ethylidenebis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)zirconium dichloride

[0204] ethylidenebis(2-n-propyl-4-(4′-tert-butylphenyl)indenyl)zirconium dichloride

[0205] ethylidenebis(2-n-butyl-4-(4′-tert-butylphenyl)indenyl)titanium dichloride

[0206] ethylidenebis(2-hexyl-4-(4′-tert-butylphenyl)indenyl)dibenzylzirconium

[0207] ethylidenebis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)dibenzylhafnium

[0208] ethylidenebis(2-methyl-4-(4′-tert-butylphenyl)indenyl)dibenzyltitanium

[0209] ethylidenebis(2-methyl-4-(4′-tert-butylphenyl)indenyl)zirconium dichloride

[0210] ethylidenebis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)dimethylhafnium

[0211] ethylidenebis(2-n-propyl-4-phenyl)indenyl)dimethyltitanium

[0212] ethylidenebis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)zirconium bis(dimethylamide)

[0213] ethylidenebis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)hafnium bis(dimethylamide)

[0214] ethylidenebis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)titanium bis(dimethylamide)

[0215] methylethylidenebis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)zirconium dichloride

[0216] methylethylidenebis(2-ethyl-4-(4′-tert-butylphenyl)indenyl)hafnium dichloride

[0217] Further examples are metallocenes from the above list in which “dichloride” is replaced by the following ligands:

[0218] monochloride mono(2,4-di-tert-butylphenoxide)

[0219] monochloride mono(2,6-di-tert-butylphenoxide)

[0220] monochloride mono(3,5-di-tert-butylphenoxide)

[0221] monochloride mono(2,6-di-sec-butylphenoxide)

[0222] monochloride mono(2,4-di-methylphenoxide)

[0223] monochloride mono(2,3-di-methylphenoxide)

[0224] monochloride mono(2,5-di-methylphenoxide)

[0225] monochloride mono(2,6-di-methylphenoxide)

[0226] monochloride mono(3,4-di-methylphenoxide)

[0227] monochloride mono(3,5-di-methylphenoxide)

[0228] monochloride monophenoxide

[0229] monochloride mono(2-methylphenoxide)

[0230] monochloride mono(3-methylphenoxide)

[0231] monochloride mono(4-methylphenoxide)

[0232] monochloride mono(2-ethylphenoxide)

[0233] monochloride mono(3-ethylphenoxide)

[0234] monochloride mono(4-ethylphenoxide)

[0235] monochloride mono(2-sec-butylphenoxide)

[0236] monochloride mono(2-tert-butylphenoxide)

[0237] monochloride mono(3-tert-butylphenoxide)

[0238] monochloride mono(4-sec-butylphenoxide)

[0239] monochloride mono(4-tert-butylphenoxide)

[0240] monochloride mono(2-isopropyl-5-methylphenoxide)

[0241] monochloride mono(4-isopropyl-3-methylphenoxide)

[0242] monochloride mono(5-isopropyl-2-methylphenoxide)

[0243] monochloride mono(5-isopropyl-3-methylphenoxide)

[0244] monochloride mono(2,4-bis-(2-methyl-2-butyl)phenoxide)

[0245] monochloride mono(2,6-di-tert-butyl-4-methylphenoxide)

[0246] monochloride mono(4-nonylphenoxide)

[0247] monochloride mono(l-naphthoxide)

[0248] monochloride mono(2-naphthoxide)

[0249] monochloride mono(2-phenylphenoxide)

[0250] monochloride mono(tert-butoxide)

[0251] monochloride mono(N-methylanilide)

[0252] monochloride mono(2-tert-butylanilide)

[0253] monochloride mono(tert-butylamide)

[0254] monochloride mono(di-iso-propylamide)

[0255] monochloride monomethyl

[0256] monochloride monobenzyl

[0257] monochloride mononeopentyl.

[0258] The catalyst system of the present invention is obtainable by reacting at least one Lewis base of the formula (I) and at least one organoelement compound d), obtainable by reacting at least one compound of the formula (VI) with at least one compound of the formula (IX), with a support. The product is subsequently reacted with a solution or suspension of one or more metallocene compounds of the formula (X) and, if desired, one or more organometallic compounds of the formula (III). This activation of the catalyst system can be carried out either before introduction into the reactor or else only in the reactor.

[0259] To prepare the catalyst system of the present invention, the support material is suspended in an organic solvent. Suitable solvents are aromatic or aliphatic solvents, for example hexane, heptane, toluene or xylene, or halogenated hydrocarbons such as ethylene chloride or halogenated aromatic hydrocarbons such as o-dichlorobenzene. The support can be pretreated beforehand with a compound of the formula (III). One or more compounds of the formula (I) is/are subsequently added to the suspension, with the reaction time being able to be from one minute to 48 hours, preferably from 10 minutes to 2 hours. The reaction product can be isolated and subsequently resuspended or else can be reacted directly with at least one of the cocatalytically active organoboron-aluminum compounds d). The reaction time here is from one minute to 48 hours, preferably from 10 minutes to 2 hours. Preference is given to using from 0.1 to 4 equivalents of a Lewis base of the formula (I) per equivalent of the organoboron-aluminum compound d). Particular preference is given to using from 0.5 to 1 equivalent of a Lewis base of the formula (I) per equivalent of organoboron-aluminum compound d). The reaction product of this reaction is a compound which is capable of forming metallocene ions and is covalently bound to the support material. This is hereinafter referred to as the modified support material. The reaction mixture is subsequently filtered and the solid is washed with one of the abovementioned solvents. The modified support material is then dried in a high vacuum. The modified support material can be resuspended after drying and be after-treated with a compound of the formula (III). However, the compound of the formula (III) can also be added before filtration and drying of the modified support material.

[0260] The application of one or more metallocene compounds, preferably of the formula (X), and one or more organometallic compounds of the formula (III) to the modified support material is preferably carried out by dissolving or suspending one or more metallocene compounds of the formula (X) in one of the above-described solvents and subsequently reacting it with one or more compounds of the formula (III) which is/are preferably likewise in dissolved or suspended form. The stoichiometric ratio of metallocene compound of the formula (X) to the organometallic compound of the formula (III) is from 100:1 to 10⁻⁴:1. The ratio is preferably from 1:1 to 10⁻²:1. The modified support material can either be placed directly in the polymerization reactor or in a reaction flask in one of the abovementioned solvents. This is followed by the addition of the mixture of a metallocene compound of the formula (X) and an organometallic compound of the formula (III). However, if desired, one or more metallocene compounds of the formula (X) can also be added to the modified support material without prior addition of an organometallic compound of the formula (III).

[0261] The ratio of modified support to metallocene compound of the formula (X) is preferably from 10 g:1 μmol to 10⁻² g:1 μmol. The stoichiometric ratio of metallocene compound of the formula (X) to units of the organoboron-aluminum compound d), of which the supported cocatalytically active organoelement compound is made up, is from 100:1 to 10⁻⁴:1, preferably from 1:1 to 10⁻²:1.

[0262] All of the above-described reactions for preparing the catalyst system of the present invention are preferably carried out at from −40 to 110° C., particularly preferably from −10° C. to 70° C.

[0263] The supported catalyst system can be used directly for polymerization. However, it is also possible to remove the solvent and resuspend the catalyst system before use in the polymerization. The advantage of this activation method is that it offers the option of allowing the polymerization-active catalyst system to be formed only in the reactor. This prevents occurrence of partial decomposition when introducing the air-sensitive catalyst.

[0264] Furthermore, the invention provides a process for preparing an olefin polymer in the presence of the catalyst system of the present invention. The polymerization can be a homopolymerization or a copolymerization. Preference is given to preparing homopolymers or copolymers of propylene.

[0265] Preference is given to polymerizing olefins of the formula R^(═)—CH═CH—R^(β), where R^(α) and R^(β) are identical or different and are each a hydrogen atom, a halogen atom, an alkoxy, hydroxy, alkylhydroxy, aldehyde, carboxyl or carboxylic ester group or a saturated or unsaturated hydrocarbon radical having from 1 to 20 carbon atoms, in particular from 1 to 10 carbon atoms, which may be substituted by an alkoxy, hydroxyl, alkylhydroxy, aldehyde, carboxyl or carboxylic ester group, or R^(α) and R^(β) together with the atoms connecting them form one or more rings. Examples of such olefins are 1-olefins, such as ethylene, propylene, 1-butene, 1-hexene, 4-methyl-1-pentene, 1-octene, styrene, cyclic olefins, such as norbornene, vinylnorbornene, tetracyclododecene, ethylidenenorbornene, dienes such as 1,3-butadiene or 1,4-hexadiene, biscyclopentadiene or methyl methacrylate.

[0266] In particular, propylene or ethylene are homopolymerized, ethylene is copolymerized with one or more C₃-C₂₀-1-olefins, in particular propylene, and/or one or more C₄-C₂₀-dienes, in particular 1,3-butadiene, or norbornene and ethylene are copolymerized.

[0267] The polymerization is preferably carried out at from −60 to 300° C., particularly preferably from 30 to 250° C. The pressure is from 0.5 to 2500 bar, preferably from 2 to 1500 bar. The polymerization can be carried out continuously or batchwise, in one or more stages, in solution, in suspension, in the gas phase or in a supercritical medium.

[0268] The supported catalyst system can either be formed directly in the polymerization system or can be resuspended as powder or while still moist with solvent and introduced into the polymerization system as a suspension in an inert suspension medium.

[0269] A prepolymerization can be carried out by means of the catalyst system of the present invention. The prepolymerization is preferably carried out using the (or one of the) olefin(s) used in the polymerization.

[0270] To prepare olefin polymers having a broad molecular weight distribution, preference is given to using catalyst systems comprising two or more different transition metal compounds, e.g. metallocenes, and/or two or more different cocatalytically active organoelement compounds.

[0271] To remove catalyst poisons present in the olefin, purification using an aluminum alkyl, for example trimethylaluminum, triethylaluminum or triisobutylaluminum, is advantageous. Either this purification can be carried out in the polymerization system itself or the olefin is brought into contact with the Al compound and subsequently separated off again before introduction into the polymerization system.

[0272] As molar mass regulator and/or to increase the activity, hydrogen is added if necessary. The total pressure in the polymerization system is from 0.5 to 2500 bar, preferably from 2 to 1500 bar.

[0273] The compound used according to the present invention is employed in a concentration, based on the transition metal, of preferably from 10⁻³ to 10⁻⁸ mol, more preferably from 10⁻⁴ to 10⁻⁷ mol, of transition metal per dm³ of solvent or per dm³ of reactor volume.

[0274] Suitable solvents for preparing both the supported chemical compound used according to the present invention and the catalyst system of the present invention are aliphatic or aromatic solvents, for example hexane or toluene, ether solvents such as tetrahydrofuran or diethyl ether or halogenated hydrocarbons such as methylene chloride or halogenated aromatic hydrocarbons such as o-dichlorobenzene.

[0275] Before addition of the catalyst system of the present invention or before activation of the catalyst system of the present invention in the polymerization system, an alkylaluminum compound such as trimethylaluminum, triethylaluminum, triisobutylaluminum, trioctylaluminum or isoprenylaluminum can be additionally introduced into the reactor to make the polymerization system inert (for example to remove catalyst poisons present in the olefin). This is added to the polymerization system in a concentration of from 200 to 0.001 mmol of Al per kg of reactor contents. Preference is given to using triisobutylaluminum and triethylaluminum in a concentration of from 10 to 0.01 mmol of Al per kg of reactor contents, as a result of which a low molar Al/M¹ ratio can be chosen in the synthesis of a supported catalyst system.

[0276] Furthermore; an additive such as an antistatic can be used in the process of the present invention, for example to improve the particle morphology of the olefin polymer. In general, it is possible to use all antistatics which are suitable for polymerization. Examples are salt mixtures of calcium salts of Medialan acid and chromium salts of N-stearylanthranilic acid, as described in DE-A-3,543,360. Further suitable antistatics are, for example, isopropanol, C₁₂-C₂₂-fatty acid soaps of alkali metals or alkaline earth metals, salts of sulfonic esters, esters of polyethylene glycols and fatty acids, polyoxyethylene alkyl ethers, etc. A review of antistatics is given in EP-A-0,107,127.

[0277] Furthermore, a mixture of a metal salt of Medialan acid, a metal salt of anthranilic acid and a polyamine can be used as antistatic, as described in EP-A-0,636,636.

[0278] Commercially available products such as Stadis® 450 from DuPont, namely a mixture of toluene, isopropanol, dodecylbenzenesulfonic acid, a polyamine, a copolymer of 1-decene and SO₂ and also 1-decene, or ASA®-3 from Shell and Atmer 163 from ICI can likewise be used.

[0279] The antistatic is preferably used as a solution; in the preferred case of isopropanol, Stadis® 450 and Atmer 163 are preferably used in an amount of from 1 to 50% by weight of this solution, preferably from 5 to 25% by weight, based on the mass of the supported catalyst (support with covalently bound compound capable of forming metallocene ions and one or more metallocene compounds, e.g. of the formula (X)) used. However, the amounts of antistatic required can vary within a wide range, depending on the type of antistatic used.

[0280] The actual polymerization is preferably carried out in liquid monomers (bulk) or in the gas phase.

[0281] The antistatic can be introduced into the polymerization at any point in time. For example, a preferred procedure is to resuspend the supported catalyst system in an organic solvent, preferably alkanes such as heptane or isododecane. It is subsequently introduced into the polymerization autoclave while stirring. The antistatic is then added. The polymerization is carried out at from 0 to 100° C. A further preferred procedure is to introduce the antistatic into the polymerization autoclave before addition of the supported catalyst system. The resuspended supported catalyst system is subsequently added while stirring at from 0 to 100° C. The polymerization time can be in the range from 0.1 to 24 hours. preference is given to a polymerization time in the range from 0.1 to 5 hours.

[0282] In the above-described process, no deposits are formed in the reactor, no agglomerates are formed and the productivity of the catalyst system used is high. The polymers prepared by the process of the present invention have a narrow molecular weight distribution and a good particle morphology.

[0283] The following examples illustrate the invention.

[0284] General procedures: Preparation and handling of the compounds were carried out under argon with exclusion of air and moisture (Schlenk technique). All solvents required were dried before use by boiling for a number of hours over suitable desiccants and subsequently distilling them under argon.

EXAMPLE 1 Synthesis of bis(dimethylaluminoxy)pentafluorophenylborane

[0285] 10 ml of trimethylaluminum (2M in toluene, 20 mmol) and 40 ml of toluene are placed in a reaction vessel. At −10° C., 2.1 g of pentafluoroboronic acid (10 mmol) in 50 ml of toluene are added dropwise to this solution over a period of 15 minutes. The mixture is stirred for 1 hour at −10° C. and subsequently for a further hour at room temperature (RT). The slightly turbid, light-yellow solution is filtered through a G4 frit. This gives a clear, light-yellow solution (0.1M based on boron) of bis(dimethylaluminoxy)pentafluorophenylborane in toluene.

EXAMPLE 2 Synthesis of di[bis(pentafluorophenyl)boroxy]methylalane

[0286] 5 ml of trimethylaluminum (2M in toluene, 10 mmol) and 45 ml of toluene are placed in a reaction vessel. At −10° C., 6.92 g of bis(pentafluorophenyl)borinic acid (20 mmol) in 50 ml of toluene are added dropwise to this solution over a period of 15 minutes. The mixture is stirred for 0.5 hour at −10° C. and subsequently for a further hour at room temperature. The slightly turbid, light-yellow solution is filtered through a G4 frit. This gives a clear, light-yellow solution (0.1M based on Al) of di([bis(pentafluorophenyl)boroxy]methylalane in toluene.

EXAMPLE 2A Synthesis of di[bis(pentafluorophenyl)boroxy]methylalane

[0287] 5 ml of trimethylaluminum (2M in toluene, 10 mmol) and 45 ml of toluene are placed in a reaction vessel. At 25° C., 6.92 g of bis(pentafluorophenyl)borinic acid (20 mmol) in 50 ml of toluene are added dropwise to this solution over a period of 15 minutes. The mixture is stirred for 1 hour at 25° C. The slightly turbid, light-yellow solution is filtered through a G4 frit. This gives a clear, light-yellow solution (0.1M based on Al) of di([bis(pentafluorophenyl)boroxy]methylalane in toluene.

EXAMPLE 3 Reaction of tris(pentafluorophenyl)borane and bis(pentafluorophenyl)borinic acid with Trimethylaluminum

[0288] 5 ml of trimethylaluminum (2M in toluene, 10 mmol) and 40 ml of toluene are placed in a reaction vessel. At −10° C., a mixture of 6.92 g of bis(pentafluorophenyl)borinic acid (20 mmol) and 5.12 g of tris(pentafluorophenyl)borane (10 mmol) in 50 ml of toluene is added dropwise to this solution over a period of 15 minutes. The mixture is stirred for 0.5 hour at −10° C. and subsequently for a further hour at room temperature. The slightly turbid, light-yellow solution is filtered through a G4 frit. This gives a clear, light-yellow toluene solution.

EXAMPLE 4 Application of bis(dimethylaluminoxy)pentafluorophenylborane to a Support

[0289] 2 g of SiO₂ (PQ MS3030, pretreated at 140° C., 10 mbar, 10 hours) are suspended in 30 ml of toluene, and at room temperature 0.6 ml of N,N-dimethylbenzylamine is added. The mixture is cooled to 0° C. and 50 ml of the solution prepared in Example 1 are added dropwise from a dropping funnel. The mixture is allowed to warm to room temperature and is stirred for another three hours. The suspension is subsequently filtered and the solid is washed with pentane. The residue is then dried to constant weight in an oil pump vacuum. This gives 3.03 g of a white support material.

EXAMPLE 5 Application of di[bis(pentafluorophenyl)boroxy]methylalane to a Support

[0290] 2 g of SiO₂ (PQ MS3030, pretreated at 140° C., 10 mbar, 10 hours) are suspended in 30 ml of toluene and, at room temperature 0.48 ml of N,N-dimethylbenzylamine is added. The mixture is cooled to 0° C. and 40 ml of the solution prepared in Example 2 are added dropwise from a dropping funnel. The mixture is allowed to warm to room temperature and is stirred for another three hours. The suspension is subsequently filtered and the solid is washed with pentane. The residue is then dried to constant weight in an oil pump vacuum. This gives 4.01 g of a white support material.

EXAMPLE 6 Application of the Reaction Mixture from Example 3 to a Support

[0291] 2 g of SiO₂ (PQ MS3030, pretreated at 140° C., 10 mbar, 10 hours) are suspended in 30 ml of toluene, and at room temperature 0.48 ml of N,N-dimethylbenzylamine is added. The mixture is cooled to 0° C. and 40 ml of the solution prepared in Example 3 are added dropwise from a dropping funnel. The mixture is allowed to warm to room temperature and is stirred for another three hours. The suspension is subsequently filtered and the solid is washed with pentane. The residue is then dried to constant weight in an oil pump vacuum. This gives 4.5 g of a white support material.

EXAMPLE 7 Preparation of Catalyst System 1

[0292] 0.5 g of the support prepared in Example 4 are added at room temperature to 5.8 mg of dimethylsilanediylbis(2-methyl-4-phenylindenyl)dimethylzirconium (10 μmol) in 3 ml of toluene. The suspension is stirred briefly and 0.01 ml of trimethylaluminum (TMA) (2M in toluene, 20 μmol) is subsequently added. The catalyst solution is stirred for 1 hour and the solvent is then taken off in an oil pump vacuum. This gives an orange, free-flowing powder.

EXAMPLE 8 Preparation of Catalyst System 2

[0293] 7 mg of dimethylsilanediylbis(2-methyl-4-(4′-tert-butylphenylindenyl)zirconium dichloride (10 μmol) in 5 ml of toluene are stirred for 40 minutes with 0.02 ml of TMA (2M in toluene, 40 μmol). 0.44 g of the support prepared in Example 5 are subsequently added at room temperature. The catalyst solution is stirred for 1 hour and the solvent is then taken off in an oil pump vacuum. This gives an orange, free-flowing powder.

EXAMPLE 9 Preparation of Catalyst System 3

[0294] 0.2 g of the support prepared in Example 6 is added at room temperature to 3.3 mg of dimethylsilanediylbis(2-methyl-4-(4′-tert-butylphenylindenyl)dimethyl zirconium (5 μmol) in 3 ml of toluene. The catalyst solution is stirred for 1 hour and the solvent is then taken off in an oil pump vacuum. This gives an orange, free-flowing powder.

EXAMPLE 10 Polymerization Using Catalyst System 1

[0295] A dry 2 l reactor is flushed firstly with nitrogen and subsequently with propylene and charged with 1.5 l of liquid propylene. 3 ml of triisobutylaluminum (TIBA) (20% strength in Varsol) are added thereto and the mixture is stirred for 15 minutes. The catalyst system 1 prepared in Example 7 is subsequently injected as a suspension in 20 ml of heptane and rinsed in with 15 ml of heptane. The reaction mixture is heated to the polymerization temperature of 60° C. and polymerization is carried out for 1 hour. The polymerization is stopped by venting the remaining propylene. The polymer is dried in a vacuum drying oven. This gives 160 g of polypropylene powder (PP). The reactor showed no deposits on the inner wall or stirrer. The catalyst activity is 28 kg of PP/g of metallocene×h.

EXAMPLE 11 Polymerization Using Catalyst System 2

[0296] A dry 2 l reactor is flushed firstly with nitrogen and subsequently with propylene and charged with 1.5 l of liquid propylene. 3 ml of TIBA (20% strength in Varsol) are added thereto and the mixture is stirred for 15 minutes. The catalyst system 3 prepared in Example 8 is subsequently injected as a suspension in 20 ml of heptane and rinsed in with 15 ml of heptane. The reaction mixture is heated to the polymerization temperature of 60° C. and polymerization is carried out for 1 hour. The polymerization is stopped by venting the remaining propylene. The polymer is dried in a vacuum drying oven. This gives 255 g of polypropylene powder. The reactor showed no deposits on the inner wall or stirrer. The catalyst activity is 36 kg of PP/g of metallocene×h.

EXAMPLE 12 Polymerization Using Catalyst System 3

[0297] A dry 2 l reactor is flushed firstly with nitrogen and subsequently with propylene and charged with 1.5 l of liquid propylene. 3 ml of TIBA (20% strength in Varsol) are added thereto and the mixture is stirred for 15 minutes. The catalyst system 3 prepared in Example 9 is subsequently injected as a suspension in 20 ml of heptane and rinsed in with 15 ml of heptane. The reaction mixture is heated to the polymerization temperature of 60° C. and polymerization is carried out for 1 hour. The polymerization is stopped by venting the remaining propylene. The polymer is dried in a vacuum drying oven. This gives 145 g of polypropylene powder. The reactor showed no deposits on the inner wall or stirrer. The catalyst activity is 44 kg of PP/g of metallocene×h. 

We claim:
 1. A catalyst system comprising a) at least one organometallic compound, b) at least one Lewis base, c) at least one support and d) at least one organoelement compound which is the reaction product of at least one compound of the formula (VI) with at least one compound of the formula (IX),

 where R⁷ can be a hydrogen atom or a boron-free C₁-C₄₀ group such as C₁-C₂₀-alkyl, C₆-C₂₀-aryl, C₇-C₄₀-arylalkyl, C₇-C₄₀-alkylaryl, R⁴ and R⁵ are identical or different and are each a hydrogen atom, a halogen atom or a C₁-C₄₀ group or R⁴ is an —OSiR₃ group, where R are identical or different and are as defined for R⁵, X is an element of main group VI of the Periodic Table of the Elements or an NR group, where R is a hydrogen atom or a C₁-C₂₀-hydrocarbon radical such as C₁-C₂₀-alkyl or C₁-C₂₀-aryl, f is an integer from 0 to 3 g is an integer from 0 to 3, where f+g is not equal to 0, h is an integer from 1 to 10, where the organoelement compound is covalently bound to the support, wherein the Lewis base has the formula I, M¹R¹R²R³  (I)  where M¹ is an element of main group V of the Periodic Table of the Elements, R¹, R² and R³ are identical or different and are each a hydrogen atom, a C₁-C₂₀-alkyl group, a C₁-C₂₀-haloalkyl group or a C₇-C₄₀-arylalkyl group, where two radicals or all three radicals R¹, R² and R³ may be joined to one another via C₂-C₂₀ units, where at least one radical R¹, R² or R³ is a C₇-C₄₀-arylalkyl group.
 2. A catalyst system as claimed in claim 1, wherein benzyl is used as a C₇-C₄₀-arylalkyl group in the Lewis base of the formula I.
 3. A catalyst system as claimed in claim 1 or 2, wherein the organometallic compound is a metallocene.
 4. A catalyst system as claimed in any of claims 1 to 3 which further comprises at least one organometallic compound of the formula III [M³R⁶ _(d)]_(e)  (III) where M³ is an element of main group I, II or III of the Periodic Table of the Elements, R⁶ are identical or different and are each a hydrogen atom, a halogen atom or a C₁-C₄₀ group, d is an integer from 1 to 3 and e is an integer from 1 to 4, as constituent e).
 5. A catalyst system as claimed in any of claims 1 to 4, wherein a porous inorganic or organic solid is used as support.
 6. The use of a catalyst system as claimed in any of claims 1 to 5 for preparing polyolefins.
 7. A process for preparing polyolefins, in which the polymerization is carried out in the presence of at least one catalyst system as claimed in any of claims 1 to
 5. 